| ELECTROPLATING PRODUCTS (USPM) |
|
|
|
|
|
| Tetramine Palladium(II) Chloride Solution |
| United States Precious Metals (USPM) offers Tetramine Palladium(II) Chloride Solution. It is a colorless to pale-yellow colored solution guaranteed to be not less than 100 grams/liter palladium contained. The product is manufactured in an ammonium hydroxide matrix. |
| Chemical Formula |
Pd (NH3)4Cl2 |
| pH |
8.5 - 10.5 |
| Palladium |
100 grams/liter(9.5% by weight max) |
| Aluminum |
< 10 ppm |
| Calcium |
< 20 ppm |
| Copper |
< 5 ppm |
| Gold |
< 20 ppm |
| Iron |
< 10 ppm |
| Lead |
< 5 ppm |
| Magnesium |
< 10 ppm |
| Manganese |
< 5 ppm |
| Nickel |
< 5 ppm |
| Silicon |
< 50 ppm |
| Sodium |
< 1000 ppm |
| Silver |
< 20 ppm |
|
| Tetrammine Palladium Sulfate Crystals |
| United States Precious Metals (USPM) offers Tetrammine Palladium Sulfate Crystals. Each lot will be accompanied by a Certificate of Analysis and packaged 5 TO metal per container. |
| Chemical Formula |
[Pd(NH3)4]SO4 |
| CAS Number |
13601-06-4 |
| Formula Weight |
271.4 |
| Description |
Pale Yellow Crystal |
| Gold, ppm OSB |
max 15 ppm |
| Silver, ppm OSB |
max 15 ppm |
| Cadmium, ppm OSB |
max 15 ppm |
| Copper, ppm OSB |
max 15 ppm |
| Iron, ppm OSB |
max 15 ppm |
| Lead, ppm OSB |
max 15 ppm |
| Ruthenium, ppm OSB |
max 50 ppm |
| Tin, ppm OSB |
max 50 ppm |
| Zinc, ppm OSB |
max 5 ppm |
| Chlorides, ppm OSB |
max 600 ppm |
|
| Rhoduna® TD |
| United States Precious Metals (USPM) offers Rhoduna® TD. Rhoduna® TD deposits brilliant-white coatings up to a thickness of approximately 0.5 µm. It is additionally characterized by high covering speed and excellent throwing power. |
| Rhodium content |
2 g/l (1-3 g/l) |
| pH value |
< 1 |
| Temperature |
40oC (RT - 65oC) |
| Current density |
1 -2 A/dm2 (0.5 - 10 A/dm2) |
| Deposition speed |
7.5 mg Rhodium/Amin at 1 A/dm2 ; at 40o C
|
| Coating |
Rhodium |
| Color |
Brilliant white |
| Hardness |
~ 800 - 900 HV |
| Density of coating |
~ 12 g/cm3 |
| Maximum coating thickness |
~ 0.5 µm |
|
| Platinum Clad Niobium Mesh Anodes |
| United States Precious Metals (USPM) offers Platinum Clad Niobium Mesh Anodes. Platinum clad niobium (columbium) expanded mesh anodes are available in widths of 6" and continuous lengths up to 72".
Prior to expansion, 99.95% pure platinum metal is clad onto one side of the niobium substrate (SC, single clad) or onto both sides of the niobium substrate (DC, double clad) in thicknesses of: |
- 125 µ" Pt (3.125 µ ) single clad (SC)
- 250 µ" Pt (6.25 µ ) single clad (SC)
|
- 125 µ" Pt (3.125 µ ) double clad (DC)
- 250 µ" Pt (6.5 µ ) double clad (DC)
|
| The platinum clad anodes can be made rigid by framing them in a "U" shaped channel of 1" wide titanium metal. Titanium straps of any length can be welded to the platinum clad anodes. The platinum plated clad anodes CANNOT be returned for "re-cladding" when the original Pt thickness wears out. |
| Platinum Plated Titanium Anodes |
| United States Precious Metals (USPM) offers Platinum Plated Titanium Anodes. Platinum plated titanium anodes are available in lengths up to 50" and widths as small as 1". 99.95 % pure platinum metal is electrodeposited on the titanium substrate in thicknesses of: |
- 50 µ" Pt (1.25 µ )
- 100 µ" Pt (2.5 µ )
- 150 µ" Pt (3.75 µ )
|
| The standard titanium substrate is 0.035 gauge. Other titanium thicknesses are available. 1" wide Titanium straps of any length can be welded to the platinum plated anodes. The platinum plated anodes can be returned for "re-plating" when the original Pt thickness wears out. |